Art Texture Powder
Coating |
| |
|
|
HS Code: |
3907300090 |
|
Brand: |
Kianco |
|
Origin: |
China |
|
Method: |
Spray |
|
Use: |
Powder Coating |
|
Level: |
Finish Coat |
|
Substrate: |
Steel |
|
Appearance: |
Powder |
|
Packing: |
Two Layers of Poly bag Inner, Paper Carton Outer |
|
|
|
Description:
01.General instruction of epoxy/polyester powder coating is based on
epoxy and polyester resin-based material obtained, which provides a
variety of colors, as compared with pure epoxy powder has good heat
resistance and light resistance
02.Application: typical applicable to those where a tough decorative
finish is desirable such as domestic appliances and office
furniture, also applicable to a variety of equipment, pipes, pipe
fittings and other requirements of corrosion coating.
03.Variety gloss and color: high gloss (Above 85º), semi gloss
(10~85º)and no gloss (below 10º), gloss and color of product is made
according to clients requirement.
04.Curing Condition: Standard curing and lower temperature curing is
available.
05.Surface: Various kinds of art texture products are available,
such as sandy, wrinkle, hammer tone, metal effect, etc.
06.Storage: The product has a shelf life of 24 months stored in
ventilated dry and clean room with the temperature below 25°C.
07.Package: a. Inner packing: plastic bag;
b. Outer packing: paper carton;
c. NW: 20kg/carton;
d. Carton dimension: 38*28*30cm.
| Inspection Item
|
Test Standard or Method
|
Test Indicator
|
| Impact resistance
|
GB/T1732-1993
|
40cm
|
|
Cupping test
|
GB/T9753-1988 |
5mm |
| Adhesion (Planning grid method)
|
GB/T9286-1998 |
Grade 0 |
| Crook
|
GB/T6742-1986 |
3mm |
| Pencil hardness
|
GB/T6739-1996 |
H-2H |
| Salt test
|
GB/T1771-1991 |
> 500 hours
|
| Heat test
|
GB/T1740-1979 |
> 1000 hours |
|
Heat resistance
|
100°C/24 hours (white)
|
Paul Light character (best) |
| Remark
|
1, The above test use cold-rolled steel(thichness:0.8mm) to remove rust, oil. Film thickness: 50-70um.
2, All the indicators of film features will be down lightly depending on reducing of luster.
|
|
|